Reactivity at the oxygen/titania interface and the related charge transfer

The present paper reports the reactivity between TiO₂ and oxygen and the related charge transfer at 298 and 1,073 K. The studies were performed using work function measurements. It was found that oxidation of TiO₂ at 1,073 K and p(O₂)∈=∈75 kPa, initially standardized at 1,173 K and p(O₂)∈=∈10Pa, results in work function changes that are consistent with the theoretical model of the charge transfer during oxygen chemisorption and oxygen incorporation at the absence of structural transitions. However, oxidation of TiO₂ at 298K, p(O ₂)∈=∈75kPa, which has been initially standardized at 1,173K in extremely reducing conditions at p(O₂)=∼ 10^-10Pa, results in work function changes that are consistent with low-dimensional structural changes of the surface layer. It is shown that oxidation of strongly reduced TiO₂ at 298K results in a decrease of work function, which cannot be explained without assuming the structural changes of the outermost surface layer.